Ultramid 1503-2 BLACK ND3007 - 巴斯夫黑色GF33尼龙-苏州希普能塑料有限公司

ULTRAMID® 1503-2 BLACK ND3007

聚酰胺66（尼龙66）PA66-GF33

德国巴斯夫-BASF Corporation

Ultramid® 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6.

黄卡号码：E36632-317186

增强材料：玻璃纤维33%增强

含添加剂：热稳定剂

材料特性：热稳定

加工方法：黑色粒子注射成型

供货地区：北美洲

中国代理：苏州希普能工程塑料

ULTRAMID® 1503-2 BLACK ND3007 PA66中文物性表

机械性能	干/已调节	单位	测试标准
拉伸模量	10800/-	MPa	ISO 527-1/-2
断裂应力	190/144	MPa	ISO 527-1/-2
断裂伸长率	3/5	%	ISO 527-1/-2
简支梁缺口冲击强度,+23℃	11/-	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度,-30℃	8/-	kJ/m²	ISO 179/1eA
热性能	干/已调节	单位	测试标准
熔融温度,10℃/min	257/*	℃	ISO 11357-1/-3
热变形温度,1.80MPa	255/*	℃	ISO 75-1/-2
热变形温度,0.45MPa	264/*	℃	ISO 75-1/-2
其它性能	干/已调节	单位	测试标准
吸水性	5.7/*	%	Sim.to ISO 62
吸湿性	1.7/*	%	Sim.to ISO 62
密度	1400/-	kg/m³	ISO 1183
注塑成型 Polyamid 66 materials must be properly dried in order to provide parts with optimum strength and toughness. Polyamid 66 materials are hygroscopic and will become degraded by excessive moisture during the injection molding process. For unopened bag/box,dry at 140F (60℃) for 1-2 hours. For material exposed to the atmosphere,if additional drying is needed,dry at 150F (66℃) or until the moisture level is between 0.04-0.20%. Melt Temperature: 288–305℃(550–580F) Mold Temperature: 60–100℃(140–212F) Injection Pressure: 35–125 MPa(5000–18000 psi) Back Pressure: 0–0.35 MPa(0–50 psi) Screw RPM 40–80 Screw Compression Ratio:3:1–4:1 This product can be processed over a wide range of mold temperatures;however,for applications where aesthetics are critical,a mold surface temperature of 60-100℃ (140-212F) is recommended. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing.