VALOX™ 308
Generic Name: 聚丁烯对苯二甲酸酯(PBT) - 提供方: SABIC
PBT for compounding/fibers only. Not intended for injection molding. FDA compliant.Melt viscosity: 250C at 21.6 kgf is 1575-1950 poise. Available in Natural color (1001) only.
供货地区：北美洲、拉丁美洲
物料性能：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.31 | g/cm³ | ASTM D792,ISO 1183 |
| 熔融体积流量（MVR）(250℃/2.16kg) | 52 | cm³/10min | ISO 1133 |
| 48 | |||
| 收缩率 | 内部方法 | ||
| 垂直:3.20 mm | 1.5 到 2.0 | % | |
| 流动:3.20 mm | 1.5 到 2.0 | % | |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 0.34 | % | |
| 平衡,23℃,50% RH | 0.080 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --1 | 2600 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服2 | 58.0 | MPa | ASTM D638 |
| 屈服 | 50.0 | MPa | ISO 527-2/50 |
| 断裂2 | 26.0 | MPa | ASTM D638 |
| 断裂 | 49.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服2 | 3.7 | % | ASTM D638 |
| 屈服 | 3.2 | % | ISO 527-2/50 |
| 断裂2 | 140 | % | ASTM D638 |
| 断裂 | 8.6 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距3 | 2400 | MPa | ASTM D790 |
| --4 | 2200 | MPa | ISO 178 |
| 弯曲应力 | |||
| --4,5 | 80.0 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距3 | 83.0 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度6(23℃) | 4.0 | kJ/m² | ISO 179/1eA |
| 悬壁梁缺口冲击强度 | |||
| -30℃ | 35 | J/m | ASTM D256 |
| 23℃ | 37 | J/m | ASTM D256 |
| -30℃7 | 3.0 | kJ/m² | ISO 180/1A |
| 23℃7 | 4.0 | kJ/m² | ISO 180/1A |
| 装有测量仪表的落镖冲击(23℃,Total Energy) | 25.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 120 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,3.20 mm | 49.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距7 | 49.0 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 167 | ℃ | ASTM D15258 |
| -- | 169 | ℃ | ISO 306/B120 |
| -- | 173 | ℃ | ISO 306/B50 |
| 线形热膨胀系数 | ASTM E831,ISO 11359-2 | ||
| 流动:-40 到 40℃ | 7.6E-5 | cm/cm/℃ | |
| 垂直:-40 到 40℃ | 7.8E-5 | cm/cm/℃ | |
| 挤压说明 Compounding Extrusion Parameters Drying Temperature: 110 to 120℃ Drying Time: 4 to 6 hr Drying Time (Cumulative): 8 hr Maximum Moisture Content: 0.02% Melt Temperature: 245 to 260℃ Barrel - Zone 1 Temperature: 200 to 230℃ Barrel - Zone 2 Temperature: 240 to 255℃ Barrel - Zone 3 Temperature: 240 to 275℃ Barrel - Zone 4 Temperature: 240 to 275℃ Adapter Temperature: 240 to 275℃ Die Temperature: 240 to 275℃ Water Bath Temperature: 25 to 35℃ 备注 15.0 mm/min 2类型 1,50 mm/min 31.3 mm/min 42.0 mm/min 5at Yield 680*10*4 sp=62mm 780*10*4 mm 8速率 A (50℃/h),载荷2 (50N) |
|||
聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(PTA)或者对苯二甲酸酯(DMT)聚缩合而成，分子式为(C8H8·C4H6·C3H3N)x，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。PBT是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。