Ultraform® N 2640 Z2 UNC Q600
聚甲醛 (POM) 共聚物
德国巴斯夫-BASF Corporation
产品说明:
Ultraform N 2640 Z2 UNC Q600 is an elastomer-modified injection molding POM grade with high impact strength.
Applications
Typical applications include toys components such as bicycle frames, automotive parts such as cladding elements and windshield wiper units, and clips, snap and fastening elements, and other components subject to impact stress.
ul证书号：E36632-531689
含添加剂：冲击改性剂
材料特性：抗冲击，高抗撞击
材料用途：紧固件，汽车领域的应用，玩具
加工方法：颗粒注射成型
供货地区：北美洲
中国代理：苏州希普能工程塑料
Ultraform® N 2640 Z2 UNC Q600巴斯夫POM中文加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.37 | g/cm³ | ASTM D792,ISO 1183 |
| 熔融体积流量（MVR）(190℃/2.16kg) | 7.0 | cm³/10min | ISO 1133 |
| 收缩率 | |||
| 流动:3.18 mm | 1.9 | % | |
| 垂直 | 1.9 | % | ISO 294-4 |
| 流动 | 1.9 | % | ISO 294-4 |
| 吸水率 | |||
| 饱和 | 0.80 | % | ASTM D570 |
| 饱和,23℃ | 0.80 | % | ISO 62 |
| 平衡,50% RH | 0.20 | % | ASTM D570 |
| 平衡,23℃,50% RH | 0.20 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 2000 | MPa | ISO 527-1 |
| 抗张强度 | |||
| 屈服,23℃ | 50.0 | MPa | ASTM D638,ISO 527-2 |
| 屈服,-40℃ | 80.0 | MPa | ISO 527-2 |
| 伸长率(屈服,23℃) | 12 | % | ASTM D638,ISO 527-2 |
| 标称拉伸断裂应变(23℃) | 45 | % | ISO 527-2 |
| 拉伸蠕变模量 | ISO 899-1 | ||
| 1 hr | 1550 | MPa | |
| 1000 hr | 1050 | MPa | |
| 弯曲模量(23℃) | 1970 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | ||
| -30℃ | 6.5 | kJ/m² | |
| 23℃ | 11 | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179 | ||
| -30℃ | 230 | kJ/m² | |
| 23℃ | 无断裂 | ||
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -40℃ | 69 | J/m | |
| 23℃ | 120 | J/m | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火 | 140 | ℃ | ASTM D648 |
| 0.45 MPa,未退火 | 150 | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 85 | ℃ | ASTM D648,ISO 75-2/A |
| 熔融峰值温度 | 167 | ℃ | ASTM D3418,ISO 3146 |
| 线形热膨胀系数-流动 | |||
| -- | 7.0E-5 | cm/cm/℃ | ASTM E831 |
| -- | 1.2E-4 | cm/cm/℃ | |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | |||
| 1.50 mm | 1.0E+14 | ohms | ASTM D257 |
| -- | 1.0E+14 | ohms | IEC 60093 |
| 体积电阻率 | |||
| 1.50 mm | 1.0E+14 | ohms·cm | ASTM D257 |
| -- | 1.0E+14 | ohms·cm | IEC 60093 |
| 介电强度 | 40 | kV/mm | IEC 60243-1 |
| 介电常数 | IEC 60250 | ||
| 100 Hz | 4.00 | ||
| 1 MHz | 4.00 | ||
| 耗散因数 | IEC 60250 | ||
| 100 Hz | 0.010 | ||
| 1 MHz | 0.014 | ||
| 漏电起痕指数 | 600 | V | IEC 60112 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 80到110 | ℃ | |
| 干燥时间 | 2.0到4.0 | hr | |
| 建议的最大水分含量 | 0.15 | % | |
| 加工（熔体）温度 | 190到230 | ℃ | |
| 模具温度 | 60到120 | ℃ | |
| 注塑压力 | 3.50到7.00 | MPa | |