Ultradur® S 4090 G4 BK15051
聚对苯二甲酸丁二酯+ASA (PBT+ASA)
德国巴斯夫-BASF Corporation
产品说明:
Ultradur S 4090 G4 BK15051 is a 20% glass reinforced, pigmented black PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage.
Applications
Applications include highly stressed equipment housings in the automotive, electrical and household sectors.
增强材料：玻璃纤维20%增强
材料特性：低翘曲，耐化学品良好，收缩性低，优良外观，Good ESCR (Stress Crack Resist.)
材料用途：电器外壳，家用货品，汽车领域的应用，外壳
加工方法：黑色粒子注射成型
供货地区：北美洲
中国代理：苏州希普能工程塑料
Ultradur® S 4090 G4 BK15051巴斯夫中文加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.38 | g/cm³ | ISO 1183 |
| 熔融体积流量（MVR）(275℃/2.16kg) | 15 | cm³/10min | ISO 1133 |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 0.40 | % | |
| 平衡,23℃,50% RH | 0.20 | % | |
| Viscosity Number (Reduced Viscosity) | 108.0 | ml/g | ISO 1628 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 7000 | MPa | ISO 527-1 |
| 拉伸应力(断裂,23℃) | 108 | MPa | ISO 527-2 |
| 拉伸应变(断裂,23℃) | 2.4 | % | ISO 527-2 |
| 弯曲模量(23℃) | 6400 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度(23℃) | 7.0 | kJ/m² | ISO 179 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度(1.8MPa,未退火) | 184 | ℃ | ISO 75-2/A |
| 溶融温度（DSC） | 223 | ℃ | ISO 3146 |
| 线形热膨胀系数-流动 | 4.0E-5 | cm/cm/℃ | |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 100 到 120 | ℃ | |
| 干燥时间 | 4.0 | hr | |
| 建议的最大水分含量 | 0.040 | % | |
| 加工（熔体）温度 | 250 到 270 | ℃ | |
| 模具温度 | 60 到 100 | ℃ | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背压 | < 1.00 | MPa | |