Ultradur® S 4090 G6
聚对苯二甲酸丁二酯+ASA (PBT+ASA)
德国巴斯夫-BASF Corporation
产品说明:
Ultradur S 4090 G6 is a 30% glass reinforced PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage.
Applications
Applications include highly stressed equipment housings in the automotive, electrical and household sectors.
ul证书号：E41871-233618
增强材料：玻璃纤维30%增强
材料特性：低翘曲，耐化学品性能良好，收缩性低，优良外观，Good ESCR (Stress Crack Resist.)
材料用途：电器外壳，家用货品，汽车领域的应用，外壳
加工方法：粒子注射成型
供货地区：北美洲，欧洲，亚太地区
中国代理：苏州希普能工程塑料
Ultradur® S 4090 G6巴斯夫中文加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.47 | g/cm³ | ASTM D792,ISO 1183 |
| 收缩率 | |||
| 流动:3.18 mm | 0.30 | % | |
| 垂直 | 0.75 | % | ISO 294-4 |
| 流动 | 0.29 | % | ISO 294-4 |
| 吸水率 | |||
| 饱和 | 0.40 | % | ASTM D570 |
| 饱和,23℃ | 0.40 | % | ISO 62 |
| 平衡,50% RH | 0.20 | % | ASTM D570 |
| 平衡,23℃,50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 105.0 | ml/g | ISO 1628 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 9700 | MPa | ISO 527-1 |
| 抗张强度 | |||
| 断裂,23℃ | 125 | MPa | ASTM D638,ISO 527-2 |
| 断裂,-40℃ | 195 | MPa | ISO 527-2 |
| 断裂,80℃ | 79.0 | MPa | ISO 527-2 |
| 断裂,120℃ | 47.0 | MPa | ISO 527-2 |
| 断裂,150℃ | 35.0 | MPa | ISO 527-2 |
| 伸长率 | |||
| 断裂,23℃ | 2.2 | % | ASTM D638,ISO 527-2 |
| 断裂,-40℃ | 2.4 | % | ISO 527-2 |
| 断裂,80℃ | 3.6 | % | ISO 527-2 |
| 断裂,120℃ | 5.9 | % | ISO 527-2 |
| 断裂,150℃ | 4.8 | % | ISO 527-2 |
| 拉伸蠕变模量 | ISO 899-1 | ||
| 1 hr | 7600 | MPa | |
| 1000 hr | 6700 | MPa | |
| 弯曲模量 | |||
| 23℃ | 8270 | MPa | ASTM D790 |
| 23℃ | 8300 | MPa | ISO 178 |
| 弯曲强度(23℃) | 194 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度(23℃) | 9.0 | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度 | ISO 179 | ||
| -30℃ | 50 | kJ/m² | |
| 23℃ | 59 | kJ/m² | |
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -40℃ | 69 | J/m | |
| 23℃ | 85 | J/m | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火 | 210 | ℃ | ASTM D648,ISO 75-2/B |
| 1.8 MPa,未退火 | 177 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 175 | ℃ | ISO 75-2/A |
| 熔融峰值温度 | 223 | ℃ | ASTM D3418,ISO 3146 |
| 线形热膨胀系数-流动 | 4.0E-5 | cm/cm/℃ | |
| RTI Elec | UL 746B | ||
| 0.69 mm | 130 | ℃ | |
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| RTI Imp | UL 746B | ||
| 0.69 mm | 90.0 | ℃ | |
| 1.5 mm | 90.0 | ℃ | |
| 3.0 mm | 90.0 | ℃ | |
| RTI | UL 746B | ||
| 0.69 mm | 130 | ℃ | |
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | |||
| 1.50 mm | 1.0E+14 | ohms | ASTM D257 |
| -- | 1.0E+14 | ohms | IEC 60093 |
| 体积电阻率 | |||
| 1.50 mm | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| 介电常数 | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.70 | ||
| 耗散因数 | IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.018 | ||
| 漏电起痕指数 | 500 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 0.69 mm | HB | ||
| 1.5 mm | HB | ||
| 3.0 mm | HB | ||
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 100到120 | ℃ | |
| 干燥时间 | 4.0 | hr | |
| 建议的最大水分含量 | 0.040 | % | |
| 加工（熔体）温度 | 250到270 | ℃ | |
| 模具温度 | 60到100 | ℃ | |
| 注塑压力 | 3.50到12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背压 | < 1.00 | MPa | |