SABIC VALOX™ SHF4320
聚丁烯对苯二甲酸酯(PBT)
VALOX SHF4320 is a 10% glass fibre reinforced PBT injection moulding resin with excellent electrical properties combined with good flow, mechanical and heat characteristics.
Applications: Thin wall (high voltage) automotive connectors.
黄卡号码：E45329-104622916
材料用途：薄壁(高压)汽车连接器
供货地区：欧洲
物料性能：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.35 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔体流动速率）(250℃/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| 熔融体积流量（MVR）(250℃/2.16 kg) | 23 | cm³/10min | ISO 1133 |
| 收缩率 | 内部方法 | ||
| 流动 | 0.70 到 1.1 | % | |
| 垂直 | 1.1 到 1.5 | % | |
| 吸水率 | |||
| 24 hr,23℃ | 0.18 | % | ASTM D570 |
| 24 hr,23℃,50% RH | 0.060 | % | ASTM D570 |
| 饱和,23℃ | 0.20 | % | ISO 62 |
| 平衡,23℃,50% RH | 0.070 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --1 | 4400 | MPa | ASTM D638 |
| -- | 4350 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服2 | 80.0 | MPa | ASTM D638 |
| 屈服 | 80.0 | MPa | ISO 527-2/5 |
| 断裂2 | 80.0 | MPa | ASTM D638 |
| 断裂 | 80.0 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服2 | 3.4 | % | ASTM D638 |
| 屈服 | 3.4 | % | ISO 527-2/5 |
| 断裂2 | 3.4 | % | ASTM D638 |
| 断裂 | 3.4 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距3 | 3700 | MPa | ASTM D790 |
| --4 | 3750 | MPa | ISO 178 |
| 弯曲应力 | |||
| --4,5 | 115 | MPa | ISO 178 |
| --4,6 | 120 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距3 | 120 | MPa | ASTM D790 |
| 断裂,50.0 mm 跨距3 | 112 | MPa | ASTM D790 |
| 弯曲应变 - at Break7 | 5.0 | % | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度8 | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| 简支梁无缺口冲击强度8 | ISO 179/1eU | ||
| -30℃ | 30 | kJ/m² | |
| 23℃ | 35 | kJ/m² | |
| 悬壁梁缺口冲击强度 | |||
| 23℃ | 45 | J/m | ASTM D256 |
| -30℃9 | 5.0 | kJ/m² | ISO 180/1A |
| 23℃9 | 7.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| 23℃ | 510 | J/m | ASTM D4812 |
| -30℃9 | 30 | kJ/m² | ISO 180/1U |
| 23℃9 | 35 | kJ/m² | ISO 180/1U |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度(R 计秤) | 120 | ISO 2039-2 | |
| 球压硬度(H 358/30) | 110 | MPa | ISO 2039-1 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 215 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,64.0 mm 跨距9 | 215 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 185 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距9 | 185 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 220 | ℃ | ASTM D152510,ISO 306/A5010 |
| -- | 200 | ℃ | ASTM D152511,ISO 306/B5011 |
| -- | 195 | ℃ | ISO 306/B120 |
| Ball Pressure Test(123 到 127℃) | 通过 | IEC 60695-10-2 | |
| 线形热膨胀系数 | ASTM E831,ISO 11359-2 | ||
| 流动:23 到 150℃ | 4.5E-5 | cm/cm/℃ | |
| 垂直:23 到 150℃ | 2.1E-4 | cm/cm/℃ | |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | > 1.0E+15 | ohms·cm | ASTM D257,IEC 60093 |
| 介电强度 | |||
| 0.800 mm,in Oil | 30 | kV/mm | ASTM D149 |
| 1.60 mm,in Oil | 23 | kV/mm | ASTM D149 |
| 3.20 mm,in Oil | 18 | kV/mm | ASTM D149 |
| 0.800 mm,在油中 | 30 | kV/mm | IEC 60243-1 |
| 1.60 mm,在油中 | 23 | kV/mm | IEC 60243-1 |
| 3.20 mm,在油中 | 18 | kV/mm | IEC 60243-1 |
| 介电常数 | |||
| 1 MHz | 3.40 | ASTM D150,IEC 60250 | |
| 50 Hz | 3.10 | IEC 60250 | |
| 60 Hz | 3.10 | IEC 60250 | |
| 耗散因数 | |||
| 1 MHz | 0.015 | ASTM D150,IEC 60250 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | PLC 0 | UL 746A | |
| 漏电起痕指数 | 600 | V | IEC 60112 |
| 高电弧燃烧指数(HAI)12 | PLC 0 | UL 746A | |
| 热丝引燃 (HWI) | PLC 1 | UL 746A | |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级(1.5 mm) | HB | UL 94 | |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
| 熔体粘度(260℃,1500 sec^-1) | 100 | Pa·s | ISO 11443 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
| 填充物 | 10 | % | ASTM D229 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 110 到 120 | ℃ | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 40 到 60 | ℃ | |
| 料筒后部温度 | 230 到 245 | ℃ | |
| 料筒中部温度 | 240 到 255 | ℃ | |
| 料筒前部温度 | 245 到 265 | ℃ | |
| 射嘴温度 | 240 到 260 | ℃ | |
| 加工（熔体）温度 | 250 到 270 | ℃ | |
| 模具温度 | 40 到 100 | ℃ | |
| 备注 15.0 mm/min 2类型 1, 5.0 mm/min 31.3 mm/min 42.0 mm/min 5at Break 6at Yield 72 mm/min 880*10*4 sp=62mm 980*10*4 mm 10速率 A (50℃/h), 压 力1 (10N) 11速率 A (50℃/h), 载荷2 (50N) 12Surface |
|||