Ultraform® N 2320 003 PRO AT
聚甲醛（POM）共聚物
德国巴斯夫-BASF Corporation
产品说明:
Ultraform N 2320 003 PRO AT is an unfilled injection molding POM grade, which supports customers in product development for the medical technology market. This grade complied with US Pharmacopoeia: Biological Reactivity Tests, USP Plastic Class VI (USP VI), ISO 10993-5: Biological Evaluation of Medical Devices Part 5: Test for Cytotoxicity, DMF: A Drug Master File (DMF) has been registered at FDA for Ultraform® PRO and Food Contact: Ultraform® PRO is in compliance with multiple regional food contact regulations, especially for Europe and United States.
This material can be used for functional parts in devices such as insulin pens or powder inhalers as well as for plug in connectors or medical device handles.
材料特性：食品可接触级
材料用途：医疗/护理用品
加工方法：粒子注射成型
供货地区：北美洲
中国代理：苏州希普能工程塑料
Ultraform® N 2320 003 PRO AT巴斯夫POM中文加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.41 | g/cm³ | ISO 1183 |
| 熔融体积流量（MVR）(190℃/2.16kg) | 7.5 | cm³/10min | ISO 1133 |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 0.90 | % | |
| 平衡,23℃,50% RH | 0.20 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 2700 | MPa | ISO 527-1 |
| 拉伸应力(屈服,23℃) | 64.0 | MPa | ISO 527-2 |
| 拉伸应变(屈服,23℃) | 11 | % | ISO 527-2 |
| 标称拉伸断裂应变(23℃) | 32 | % | ISO 527-2 |
| 拉伸蠕变模量(1000hr) | 1400 | MPa | ISO 899-1 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | ||
| -30℃ | 5.5 | kJ/m² | |
| 23℃ | 6.5 | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179 | ||
| -30℃ | 250 | kJ/m² | |
| 23℃ | 270 | kJ/m² | |
| 悬壁梁缺口冲击强度 | ISO 180 | ||
| -30℃ | 5.5 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度(1.8 MPa,未退火) | 95.0 | ℃ | ISO 75-2/A |
| 溶融温度（DSC） | 166 | ℃ | ISO 3146 |
| 线形热膨胀系数-流动 | 1.1E-4 | cm/cm/℃ | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | 1.0E+13 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E+13 | ohms·cm | IEC 60093 |
| 介电常数(1MHz) | 3.80 | IEC 60250 | |
| 耗散因数(1MHz) | 5.0E-3 | IEC 60250 | |
| 漏电起痕指数(解决方案A) | 600 | V | IEC 60112 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 80到110 | ℃ | |
| 干燥时间 | 2.0到4.0 | hr | |
| 建议的最大水分含量 | 0.15 | % | |
| 加工（熔体）温度 | 190到230 | ℃ | |
| 模具温度 | 60到120 | ℃ | |
| 注塑压力 | 3.50到7.00 | MPa | |